Suhm Spring Works - Materials Properties
|
Material |
Material
Properties |
Maximum
Working Temp. |
|
Modulus
of Elasticity |
Approx.
Design % of Ultimate Tensile (torsional) |
Common
Sizes, |
|
Monel
K-500 QQ-N-286 AMS 4676C UNS N05500 |
Cold
drawn. Very high corrosion resistance. Good for
use in elevated temperature applications. |
500°F |
1345/965 |
(E) 179,3k (G) 63,5k |
40% |
0,46
to 50,80 |
SIZE CHART
|
Wire Diameter, mm |
||||||
| 0,46 | 0,97 |
2,67 |
4,50 | 6,81 | 9,98 | 13,49 |
| 0,69 | 1,04 | 3,18 | 4,67 | 7,14 | 10,31 |
14,27 |
|
0,79 |
1,57 | 3,43 | 5,99 | 7,92 |
11,10 |
15,88 |
| 0,84 | 1,83 | 3,76 | 6,35 | 8,41 |
11,89 |
|
| 0,86 | 2,03 | 4,11 | 6,65 | 9,19 |
12,70 |
|
| Bar Diameter, mm |
||||||
|
17,45 |
19,05 |
22,23 |
25,40 |
31,75 |
41,28 |
47,63 |
|
18,24 |
20,62 |
23,80 |
58,58 |
38,10 |
44,45 |
50,80 |
SPECIFICATIONS
FOR MONEL K-500
|
Element |
Minimum % |
Maximum % |
|
Nickel + Cobalt |
63.00 |
70.00 |
|
Aluminum |
2.00 |
4.00 |
|
Titanium |
1.025 |
1.00 |
|
Iron |
…. |
2.00 |
|
Manganese |
…. |
1.50 |
|
Silicon |
…. |
1.00 |
|
Cobalt
(3.1.1) |
…. |
1.00 |
|
Carbon |
…. |
0.25 |
|
Zinc
(3.1.1) |
…. |
0.02 |
|
Phosphorus
(3.1.1) |
…. |
0.02 |
|
Sulfur |
…. |
0.010 |
|
Tin
(3.1.1) |
…. |
0.006 |
|
Lead
(3.1.1) |
…. |
0.006 |
|
Copper |
Remainder |
Remainder |
TENSILE
PROPERTIES
(after Precipitation Heat
Treatment)
|
Tensile
Strength, min |
965
Mpa |
|
Yield
Strength at 0.2% Offset, min. |
690
Mpa |
|
Elongation
in 50,8 mm or 4D, min |
20% (3.3.1.2.1.1) |
These data are provided as a reference guide only and are not intended for design purposes. Strength values and sizes are subject to change. Please check with a Suhm Spring representative for confirmation.
25